Phaetus DLC Hardened Steel PS Nozzle V2 (V6 style)

Wear-resistance, high temperature performance, suitable for 3D printing composites with abrasive additives such as Carbon Fiber, Steel, Wood, Boron Carbide, Tungsten and Phosphorescent pigment as well as conventional filaments. Performance Analysis

DLC coating on whole nozzle surface with its hardness HV2200, thickness 2μm, and friction coefficient 0.05; Fine finish, low adhesion, high wear resistance.

Superior quality imported high-speed steel bars, special post-treatment, high temperature hardness up to HRC62.

Overall high temperature resistance 450℃, suitable for PEEK and other special engineering plastics printing.

Min. hole diameter 0.2mm (±0.01mm) to meet special application requirements and enable high accuracy printing.

Special processing technology and post-treatment ensure fine orifice and high smooth inner hole. Product Features

- φ0.2

Min. Orifice Diameter
- ±0.01mm

Tolerance
- ≤Ra0.4μm

Inner Hole Roughness
- ≤0.02mm

Concentricity